Effect of tool pin profile on microstructure and mechanical properties of AL6063 in Friction stir processing
1. Auflage
|
39,99 € |
|
| Verlag: | Anchor Academic Publishing |
| Format: | |
| Veröffentl.: | 07.11.2017 |
| ISBN/EAN: | 9783960677055 |
| Sprache: | englisch |
| Anzahl Seiten: | 69 |
Dieses eBook erhalten Sie ohne Kopierschutz.
Beschreibungen
Friction stir processing (FSP) is a solid state process in which a non consumable stirring (rotating) tool is plunged into a work piece up to half thickness, which causes intense plastic deformation, material mixing, and thermal exposure, resulting in refinement of micro structural properties, enhancement of mechanical properties, and homogeneity of the processed (nugget) zone. The FSP technique has been successfully used for producing fine-grained structure and surface composite, modifying the microstructure of materials, synthesizing composites like metal-metal composites.
The use of FSP generates significant frictional heating and intense plastic deformation, thereby resulting in the occurrence of dynamic recrystallization in the stirred zone (SZ). Although there is still a controversy about the grain-refinement mechanism in the SZ, it is generally believed that the grain refinement is due to dynamic recrystallization. Therefore, the factors influencing the nucleation and growth of the dynamic recrystallization will determine the resultant grain microstructure in the SZ. It has been demonstrated that the FSP parameters, tool geometry, material chemistry, workpiece temperature, vertical pressure, and active cooling exert a significant effect on the size of the recrystallized grains in the SZ.
The use of FSP generates significant frictional heating and intense plastic deformation, thereby resulting in the occurrence of dynamic recrystallization in the stirred zone (SZ). Although there is still a controversy about the grain-refinement mechanism in the SZ, it is generally believed that the grain refinement is due to dynamic recrystallization. Therefore, the factors influencing the nucleation and growth of the dynamic recrystallization will determine the resultant grain microstructure in the SZ. It has been demonstrated that the FSP parameters, tool geometry, material chemistry, workpiece temperature, vertical pressure, and active cooling exert a significant effect on the size of the recrystallized grains in the SZ.
Diese Produkte könnten Sie auch interessieren:
Neutron Applications in Earth, Energy and Environmental Sciences
von: Liyuan Liang, Romano Rinaldi, Helmut Schober
149,79 €
Nanobioelectronics - for Electronics, Biology, and Medicine
von: Andreas Offenhäusser, Ross Rinaldi
96,29 €